To develop the chitosan /polyethylene glycols succinate (CH/PEG-SA) mitomycin C (MMC) film drug del ivery system and its release effect in vitro. Methods MMC loading in composite films was determined using a UV-visible spectrophotometer. Freeze-dried films (90 mg) were immersed in 1 mL PBS buffer (pH 7.4). The concentrations of
MMC releasing in vitro were calculated refer to the standard curve of relationship between the concentrations of MMC and the value of UV-visible spectrophotometer. The curve of the concentrations of MMC releasing from the films in vitro was drawn at different time. The relationship between the films, structure and the drug releasing was revealed. Results The films showed swell ing without brittleness. The equation of Linear Regression was y=0.593x3– 2.563x2 +25.944x – 0.236 (R2=1.000). The film had a good drug del ivery capabil ity. The samples weighing 20 mg were soaked into the l iquid of PBS, the releasing concentrations of MMC were 14.961 6 μg/mL at 12 days, 14.482 4 μg/mL at 18 days and 11.409 2 μg/mL at 32 days, which was higher than ID50 of MMC (10.471 3 μg/L) to fibroblast. Then MMC was released at a low concentration. The releasing concentrations of MMC was 0.179 3 μg/ mL at 60 days until being del ivered completely. Conclusion The flexibil ity is enhanced , and the mechanical function is improved, so that there is better nature of membrane. The initial burst is avoided more effectively, and the drug releasing would be maintained for a certain time.
Citation： ZHANG Yu,ZHOU Chusong,JIANG Gangbiao,YU Bo,GAO Fei,FU Dong. DEVELOPMENT OF CHITOSAN/POLYETHYLENE GLYCOLS-SUCCINATE MITOMYCIN C FILM DRUG DELIVERYSYSTEM AND RELEASING CHARACTER IN VITRO. Chinese Journal of Reparative and Reconstructive Surgery, 2008, 22(5): 543-547. doi: Copy