Objective To study the influence of in vitro force-vascularization on in vivo vascularization of porous polylactic
glycolic acid copolymer(PLGA) scaffolds with internal network channels (PPSINC). Methods After the in vitro forcevascula ization of PPSINCs covered with microvessel endothelial cells (MVEC) of mice, they were divided into two groups: the force-vascularization group (group A) and the control group with only PSINCs (group B). All the PPSINCs were planted in the mesentery of 12 mice for 2 and 4 weeks, the PPSINCs were cut out, the vascular ization of PPSINCs was investigated by histology and immunohistochemistry, and the vascularization area of the histologic section of the PPSINCswas measured with the computer-assistant image analysis system. Result After the in vitro forcevascularization of PPSINCs, the MVEC of the mice sticking on the channel wall could be seen. After the scaffold was im
planted into the mice for 2 weeks, the vascularization area of the histologic section of PPSINCs (VA) in group A (2 260.91±242.35 μm2) was compared with that in group B (823.64±81.29 μm2)，and the difference was sig nificant in statistics（P＜0.01).The VA for 4 weeks in group A (17 284.36 ±72.67 μm2) was compared with that in group B (17 041.14±81.51 μm2), and the difference was not significant in statistics（P＞0.05）.The area of the actin positivestaining (AA) in the histologi c section of PPSINCs for 2 weeks’ implantation in group A (565.22±60.58 μm2) was compared with that in group B (205.91±16.25 μm2), and the difference was signi ficant in statistics（P＜0.01). After the implantation for 4 weeks, the VA in group A (4 321.09±19.82 μm2) was compared with group B (4 260.28±27.17 μm2), and the difference was not significant in statistics（P＞0.05）. Conclusion The PPSINC is a good simple scaffold model of vasculariazation. The in vitro force-vascularization can increase the in vivo vascularization of PPSINCs in the early stage.

Citation： WU Shihe,XU Yingxin,SONG Xuhua,et al.. A STUDY ON IN VITRO FORCEVASCULARIZATION AND IN VIVO VASCULARIZATION OF POROUS POLYLACTIC／GLYCOLIC ACID COPOLYMER SCAFFOLDS WITH INTERNAL NETWORK CHANNELS. Chinese Journal of Reparative and Reconstructive Surgery, 2006, 20(2): 181-184. doi: Copy