OBJECTIVE: To explore a new method of preparing the composite of DL-polylactic acid (PDLLA), hydroxyapatite(HA), decalcium bone matrix (DBM), and to observe the degradation characteristics of PDLLA/HA/DBM in vitro. METHODS: An emulsion blend method was developed to prepare the composite of PDLLA/HA/DBM based on the weight rate of PDLLA:HA:DBM = 1.5-2:1-1.5:1. The characteristics of the particles was observed by scanning electron microscope. In vitro, PDLLA/HA/DBM and PDLLA were put into PBS(pH7.4) respectively; the pH value, weight and biomechanics of them were determined during the degradation. RESULTS: Without heating, the emulsion blend method could be developed to prepare PDLLA/HA/DBM. Scanning electron microscope showed that the gap diameter in the compound material was 100 to 400 microns, and the porosity was 71.3%; During degradation, the pH value of PDLLA decreased little within 2 weeks, then decreased obviously and decreased to 4.0 at the end of the 4th week; while the pH value of PDLLA/HA/DBM kept quite steady and was 6.4 at the end of the 12th week. The weight of PDLLA decreased little within 4 weeks, then decreased obviously and remained 50% of its prime weight at the end of the 12th week; while the weight of PDLLA/HA/DBM decreased little within 5 weeks, then decreased obviously and remained 60% of the prime at the end of the 12th week. The prime biomechanical strength was 1.33 MPa in PDLLA and 1.71 MPa in PDLLA/HA/DBM. There was significant difference between them (P  lt; 0.05). The strength of PDLLA decreased little within 3 weeks, then decrease obviously and was 0.11 MPa at the end of the 12th week; the strength of PDLLA/HA/DBM decreased little within 4 weeks, then decrease obviously and was 0.21 MPa at the end of the 12th week. CONCLUSION: The emulsion blend method is a new method to prepare bone repair materials. As a new bone repair material, PDLLA/HA/DBM is suitable for bone tissue engineering for its good characteristics of porosity and degeneration.

Citation： ZHAO Jian hua,LIAO Wei hong,WANG Yuan liang,et al.. PREPARATION AND DEGRADATION CHARACTERISTICS OF BONE REPAIR COMPOSITE--PDLLA/HA/DBM. Chinese Journal of Reparative and Reconstructive Surgery, 2003, 17(1): 61-64. doi: Copy