A mechanical study on the bones of 29 rabbits following implantation of carbontendon was carried out. The rabbits were divided into seven groups according to the observation time (2,4,6,8,12,20 and 30 weeks after operation). A bundle of artificial tendon composed of 7,000 carbon fibers was passedthrough a tunnel in the tibia, and both ends of the artificial tendon were ligated to the muscle fibers. The mechanical strength and histological structure of the carbonbone junction and their relationship were studied in each group. Carbon fiberwas split and degradated in six to eight weeks after operation. The tensile strength of carbontendon in the soft tissue was decreased from 82±4.6N in the second week to 27±5.31N and6.3±1.81N in the sixth and eighth week respectively. The tensile strength of carbontendon increased from 3.01±1.2N to 6.1±2.01N at the carbon -tendon-bone junction in the bone. The tensile strength of carbon-tendon was unsatisfactory for implantation into bone. The carbon-tendon was split and degradated and the tensile strength was not b enough to cope with the early functional exercises.

Citation： Mao Binyao,Fang Qingmin,Liu Hongtao et al.. EXPERIMENTAL STUDY ON TENSILE STRENGTH OF CARBONTENDON IMPLANTEDINTO BONE. Chinese Journal of Reparative and Reconstructive Surgery, 1996, 10(1): 9-11. doi: Copy