Objective To explore a novel nanometer biomaterial which could induce the regeneration of tooth tissues intell igently, and to evaluate the feasibil ity of using this kind of biomaterial as the scaffold for tooth tissue engineering by investigating the role it plays in tooth tissue engineering. Methods The scaffold for tooth tissue engineering containing recombinant human bone morphogenetic protein 2 (rhBMP-2) was prepared by mixing nanoscale β tricalcium phosphate (β-TCP)/collagen particles. Forty-six 8-10 weeks old specific pathogen free Sprague Dawley (SD)rats, including 34 females and 12 males, weighing 250-300 g, were involved in this study. Tooth germs were removed under a stereomicroscope from the mandible of newborn SD rat, then digested and suspended. Scanning electronic microscope (SEM), adhesion rate of cells, and MTT assay were used to evaluate the effects of the scaffold on the tooth germ cells cultured in vitro. The tissue engineered tooth germ which was constructed by tooth germ cells and scaffold was transplanted under SD rat’s kidney capsule as the experimental group (n=12); the tooth germ cells (cell-control group, n=12) or scaffold without cells (material-control group, n=4) were transplanted separately as control groups Specimens were harvested to perform general and histological observations at 4 and 8 weeks after transplantation. Results β-TCP/collagen showed a loose and porous appearance with soft texture and excellent hydrophil icity. Tooth germ cells grew well and could attach to the scaffold tightly 3 days after coculture. The adhesion rates of tooth germ cells were 27.20% ± 2.37%, 44.52% ± 1.87%, and 73.81% ± 4.15% when cocultured with scaffold for 4, 8, and 12 hours, respectively. MTT assay showed that the cell prol iferation status of experimental group was similar to that of the control group, showing no significant difference (P gt; 0.05). Some white calcified specimens could be harvested at 4-8 weeks after transplantation. At 4 weeks after transplantation some typical structures of dental cusp and enamel-dentin l ike tissues could be seen in the experimental group. Enamel-dentin l ike tissues also formed in some specimens of cell-control group, but they arranged irregularly. At 8 weeks after transplantation the enamel-dentin l ike tissue of experimental group exhibited a mature appearance and organized structure in comparison with that at 4 weeks. And mature enamel or dentin l ike tissue also could be seen in cell-control group. In contrast, there was no enamel or dentin l ike tissue in material-control group at 4 or 8 weeks after transplantation. Conclusion rhBMP-2 decorated β-TCP/collagen scaffold has good biocompatibil ity and can be used as a novel nanometer biomaterial, so it is a good choice in scaffolds for tooth tissue engineering.
Objective To investigate the feasibility of a new kind of porous β tricalcium phosphate (β-TCP) as a scaffold for the bone tissue engineering Methods The inverted phase contrast microscope was used to observe the growth of the marrow mesenchymal stem cells (MSCs) in the experimentalgroup and the control group at 10 days.In the experimental group, the MSCs were cultured with β-TCP(3 mm×3 mm×3 mm) in the 24-hole cultivation board, and in the control to control group, only MSCs were cultivated. The scanning electron microscope was used to observe growth of MSCs at 6 days. Cultivated with β-TCP at 3, 6, 9, 12 days, the MTT assay was used to judge the biocompatibility. The cytotoxicity was analyzed with the method that used the different density(100%， 50%， 10%， 1%，0%) leaching liquor gained from β-TCP to raise MSCs. MSCs were induced into the osteoblasts and were mixed with β-TCP, and the composite was used to repair a large radius bone defect in the rabbit. The specimens were made at 2,6,12 weeks. The histology imageology, and the radionuclide bone scan were used to analyze the bone formation. Results Some MSCs had a good adherence 4 hours after MSCs were inoculated and had a complete adherence at 12 hours. The cells were shaped like polyangle, spindle or converge monolayer after 8-10 days. The cells in the two groups had no difference. The cell adhesion was good, when observed by the inverted phase contrast microscope and the scanning electron microscope at 6 days. MTT showed that the absorbance (A)was not statistically different between the experimental group and the control group (P＞0.05); the different density leaching liquor had no cytotoxicity at the different time points. Histology, X-ray, and CT tomograph showed that itcould repair the large radius bone defect in the rabbit and its in vivo degradationrate was the same as the bone formation rate. Conclusion The new porous β-TCP has a unique three dimensional (3D) stereochemical structure and superordinary physicochemical property, and so it is a good scaffold for the bone tissue engineering.