【Abstract】 Objective To produce a new bone tissue engineered carrier through combination of xenograft bone (X)and sodium alginate (A) and to investigate the biological character of the cells in the carrier and the abil ity of bone-forming in vivo, so as to provide experimental evidence for a more effective carrier. Methods BMSCs were extracted from 2-week-old New Zealand rabbits and the BMSCs were induced by rhBMP-2 (1 × 10-8mol/L). The second generation of the induced BMSCs was combined with 1% (V/W) A by final concentration of 1 × 105/mL. After 4-day culture, cells in gel were investigated by HE staining. The second generation of the induced BMSCs was divided into the DMEM gel group and the DMEM containing 1% A group. They were seeded into 48 well-cultivated cell clusters by final concentration of 1 × 105/mL. Seven days later, the BMP-2 expressions of BMSCs in A and in commonly-cultivated cells were compared. The second generation of the induced BMSCs was mixed with 2% A DMEM at a final concentration of 1 × 1010/mL. Then it was compounded with the no antigen X under negativepressure. After 4 days, cells growth was observed under SEM. Twenty-four nude mice were randomly divided into 2 group s (n=12).The compound of BMSCs-A-X (experimental group) and BMSCs-X (control group) with BMSCs whose final concentrat ion was 1 × 1010/mL was implanted in muscles of nude mice. Bone formation of the compound was histologically evaluated by Image Analysis System 2 and 4 weeks after the operation, respectively. Results Cells suspended in A and grew plump. Cell division and nuclear fission were found. Under the microscope, normal prol iferation, many forming processes, larger nucleus, clear nucleolus and more nuclear fission could be seen. BMP-2 expression in the DMEM gel group was 44.10% ± 3.02% and in the DMEM containing 1% A group was 42.40% ± 4.83%. There was no statistically significant difference between the two groups (P gt; 0.05). A was compounded evenly in the micropore of X and cells suspended in A 3-dimensionally with matrix secretion. At 2 weeks after the implantation, according to Image Analysis System, the compound of BMSCs-A-X was 5.26% ± 0.24% of the totalarea and the cartilage-l ike tissue was 7.31% ± 0.32% in the experimental group; the compound of BMSCs-X was 2.16% ± 0.22% of the total area and the cartilage-l ike tissue was 2.31% ± 0.21% in the control group. There was statistically significant difference between the two groups (P lt; 0.05). At 4 weeks after the operation, the compound of BMSCs-A-X was 7.26% ± 0.26% of the total area and the cartilage-l ike tissue was 9.31% ± 0.31% in the experimental group; the compound of BMSCs-X was 2.26% ± 0.28% of the total area and the cartilage-l ike tissue was 3.31% ± 0.26% in the control group. There was statistically significant difference between the two groups (P lt; 0.05). Conclusion The new carrier compounding A and no antigen X conforms to the superstructural principle of tissue engineering, with maximum cells load. BMSCs behave well in the compound carrier with efficient bone formation in vivo.
Objective To produce a decellularized cartilage matrix (DCM) and investigate its possibil ity to be used as a scaffold for tissue engineering. Methods Fresh bovine articular cartilage from knee joints was sl iced, freeze-dried and freeze-ground into fine powder, and then was treated sequentially with Trypsin, Triton X-100 and hypotonic solution for decellularization. The decellularized matrix was freeze-dried for shaping and cross-l inked by UV radiation. Histological, immunohistological, SEM, porosity assays and biomechanical assays were used to characterize the DCM. BMSCs were isolated from rabbit bone marrow aspirate and cultured in DCM extraction medium of different concentration (100%, 10% and 1%) for 0, 24, 48 and 72 hours, respectively, to detect the release rate of the lactate dehydrogenase (LDH). The DMEM medium (5% FBS) served as the control. Biocompatibil ity was evaluated using BMSCs (1 × 107/mL) cultured with DCM. Results The DCM showed white spongy appearances, and histological analysis showed that the material was constructed by cartilage particles without any cells or cell fragments left in the matrix. Immunohistology staining and alcian blue staining showed that DCM retained the collagen and glycosaminoglycan components of cartilaginous matrix. SEM scanning showed that DCM had a porous spongy-l ike structure with the aperture ranging 30-150 μm .The porosity assay showed that the average porosity was 89.37% and the average aperture was 90.8 μm. The mechanical assay showed that there was no difference for the compress module before and after the decellularization process, which was (17.91 ± 0.98) MPa and (15.12 ± 0.77) MPa, respectively (P gt; 0.05), but were both statistical different from normal articular cartilage [(26.30 ± 1.98) MPa, P lt; 0.05]. The LDH release rate in the DCM extraction medium of different concentration was not significantly different from that in the normal DMEM medium (P gt; 0.05). The cell adhesion test showed BMSCs grew well on DCM without any signs of growth inhibition. Conclusion Articular cartilage can be decellularized and fabricated into a scaffold which retains the major components of cartilaginous matrix. DCM has goodbiochemical, biophysical characteristics and good biocompatibil ity with cultured BMSCs and may be used as a novel scaffold for tissue engineering studies.
Objective To validate the advantage of repairing bone defect by staphylococcus aureus injection carried in collagen membrane. Methods Twentyfour adult New Zealand rabbits were divided into two groups randomly. After the experimental model of standard bone defect had been made by operation, collagen membrane/staphylococcus aureus injection and staphylococcus aureus injection with the same quantity were transplanted in bone defect areas of the two groups respectively. The reconstructed tissues were observed by general method, X-ray, histology, and immunohistochemistry at 2nd、4th、6th、8th week respectively. Results The experimental group showed that new bone proliferated distinctly in bone defect areaand the proliferation lasted long, and no excessive connective tissue in defectarea. X-ray observation showed that there was continual callus growth in transplantation area in early stage and the distribution of new bones was even in the group. Histological observation showed that there were many new bone growth centers in bone defect area, trabecular bones were sequentially distributed, and mature bone replacement was complete. Immunohistochemical examination showed that bone morphogenetic protein (BMP) could be seen for a long time and BMP took up a large part in the new bone tissues. Conclusion Collagen membrane could prevent parenchyma from penetrating into bone defect area and provide room for new bone growth. As the carrier of staphylococcus, collagen membrane could reduce the overflow of staphylococcus and improve its curative effect as well.
Objective To study the relation between the pathogenesis of gallstone and blood lipid and protein.Methods Then indexes of blood lipid and protein in 204 cases of gallstone patients were measured and analysed by statistical software SPSS. Results There was a significant difference between the gallstone group and control in the value of proalbumin, total cholesterol, high density lipoprotein and carrier protein B (P<0.01), the value of total protein, triglyceride, low density lipoprotein cholesterol, very low density lipoprotein cholesterol and carrier protein A1 were higher than those in the control (P<0.05). Conclusion The indexes mentioned above may play an important role in the gallstone formation.