Objective To develop three-dimensional (3D) porous nanofiber scaffold of PLGA-silk fibroincollagen and to investigate its cytocompatibil ity in vitro. Methods Method of electrostatic spinning was used to prepare 3D porous nanofiber scaffold of PLGA-silk fibroin-collagen (the experimental group) and 3D porous nanofiber scaffold of PLGA (the control group). The scaffold in each group was observed by scanning electron microscope (SEM). The parameters of scaffold fiber diameter, porosity, water absorption rate, and tensile strength were detected. SC harvested from the bilateral brachial plexus and sciatic nerve of 8 SD suckl ing rats of inbred strains were cultured. SC purity was detected by S-100 immunohistochemistry staining. The SCs at passage 4 (5 × 104 cells/mL) were treated with the scaffold extract of each group at a concentration of 25%, 50%, and 100%, respectively; the cells treated with DMEM served as blank control group. MTT method was used to detect absorbance (A) value 1, 3, 5, and 7 days after culture. The SC at passage 4 were seeded on the scaffold of the experimental and the control group, respectively. SEM observation was conducted 2, 4, and 6 days after co-culture, and laser scanning confocal microscope (LSCM) observation was performed 4 days after co-culture for the growth condition of SC on the scaffold. Results SEM observation: the scaffold in two groups had interconnected porous network structure; the fiber diameter in the experimental and the control group was (141 ± 9) nm and (205 ± 11) nm, respectively; the pores in the scaffold were interconnected; the porosity was 87.4% ± 1.1% and 85.3% ± 1.3%, respectively; the water absorption rate was 2 647% ± 172% and 2 593% ± 161%, respectively; the tensile strength was (0.32 ± 0.03) MPa and (0.28 ± 0.04) MPa, respectively. S-100 immunohistochemistry staining showed that the SC purity was 96.5% ± 1.3%. MTT detection: SC grew well in the different concentration groups and the control group, the absorbance (A) value increased over time, significant differences were noted among different time points in the same group (P lt; 0.05), and there was no significant difference between the different concentration groups and the blank control group at different time points (P gt; 0.05). SEM observation: in the experimental group, SC grew well on the scaffold, axon connection occurred 4 days after co-culture, the cells prol iferated massively and secreted matrix 6 days after co-culture, and the growth condition of the cells was better than the control group. The condition observed by LSCM 4 days after co-culture was the same as that of SEM. Conclusion The 3D porous nanofiber scaffoldof PLGA-silk fibroin-collagen prepared by the method of electrostatic spinning is safe, free of toxicity, and suitable for SC growth, and has good cytocompatibil ity and proper aperture and porosity. It is a potential scaffold carrier for tissue engineered nerve.
Objective To explore the preparing methods in vitro and test the cl inical appl icabil ity of implantation in vivo of bone marrow stromal stem cells (BMSCs)-biphasic scaffold to repair defects of cartilage and subchondral bone and tocompare the differences in repaired outcomes of composite, single biphasic scaffold and rabbits themselves. Methods The upper chondral phase and the lower osseous phase of the plugs, using poly-lactic-co-glycol ic acid (PLGA), hydroxyapatite (HA), and other biomaterials, were fused into carrier scaffold, on which collagen type I (Col I) was coated. The surface and inner structure of bi phasic scaffold were observed under scanning electron microscope (SEM). BMSCs was isolated from the bone marrow of tibia and femurs of young New Zealand rabbits using centrifuging and washing, and their morphologies and adherences were observed everyday. Then BMSCs were inoculated on the surface of scaffold to form BMSCs-scaffold composites. Osteochondral defects were surgically created on articular surface of femoral intercondyles of 30 New Zealand rabbits, which were divided into groups A, B and C. In group A, a bi phasic osteochondral composite were implanted into defect, BMSCs and biphasic cyl indrical porous plug of PLGA-HA-Col I in group B, and group C was used as a control without implant. Specimens were harvested to make macroscopic and histological observations at the 1st, 3rd, 6th, and 9th months after operation respectively; meanwhile immunohistological and micro-computed tomography (micro CT) examinations were performed and graded at the 9th month after operation. Results SEM showed an excellent connection of holes in the biphasic scaffold infiltrated by Col I. Optical microscopy and SEM showed a good growth of BMSCs in scaffold without obvious cellular morphological changes and an accumulation in the holes. Macroscopic samples showed a resistant existence of defects of group C within 9 months; the scaffold completely degenerated and chondral-l ike tissue formed on articular surface with partly collapses and irregular defects in group A; and smoother surface without collapses and approach to normal with texture of new regeneration in group B. There were statistically significant differences in macroscopic results (P lt; 0.001), group B was superior to group A, and group C was the worst. The micro CT showed good repairs and reconstruction of subchondral bone, with a acceptable integration with newborn chondral-l ike tissue and host bone in group B. Quantificational analysis of relevantparameters showed no significant differences. Histological results showed inflammations located in defects at the 1st month, new tissue grew into scaffold at the 3rd month; new chondral-l ike tissue crept on the margin of defects and biphasic scaffold degenerated completely at the 6th month, and lots of collagen formed in subchondral bone with major fibrocartilage on chondralarea at the 9th month after surgery in groups A and B. In groups A and B, immunohistological observations were weak positive for Col II and positive for Col I. Conclusion Biphasic scaffold implanted in body can induce and accelerate repair of defects of articular cartilages which are mainly filled with fibrocartilage, especially for subchondral bone. Scaffold combined with BMSCs has the best repairing effects 9 months after implantation.