ObjectiveTo explore the effect of silk fibroin/poly(L-lactic acid-co-e-caprolactone) [SF/P(LLA-CL)] nanofibrous scaffold on tendon-bone healing of rabbits.MethodsSF/P(LLA-CL) nanofibrous scaffold was fabricated by electrospinning methods. The morphology of the scaffold was observed by scanning electron microscope (SEM). Pre-osteoblasts MC3T3-E1 cells were seeded on the scaffold and cultured for 1, 3, and 5 days. Cell adhesion and proliferation were also observed by SEM. Meanwhile, twenty-four New Zealand white rabbits were randomly divided into the autogenous tendon group (control group) and the autogenous tendon wrapped with SF/P(LLA-CL) scaffold group (experimental group), with twelve rabbits in each group. An extra-articular model was established, the effect was evaluated by histological examination and mechanical testing.ResultsThe morphology of SF/P(LLA-CL) nanofibrous scaffold was random, with a diameter of (219.4±66.5) nm. SEM showed that the MC3T3-E1 cells seeded on the scaffold were in the normal shape, growing well, and proliferating with time course. The results of histological examination showed that inflammatory cells infltrated into the graft-host bone interface at 6 weeks after operation in both groups. Besides, the width of interface showed no significant difference between groups. At 12 weeks after operation, protruding new bone tissue could be observed at the interface in the experimental group, while scar tissue but no new bone tissue could be seen at the interface in the control group. Mechanical testing showed that there was no significant difference in the failure load and the stiffness between groups at 6 weeks after operation (P>0.05). The failure load and the stiffness in the experimental group were significantly higher than those in the control group at 12 weeks after operation (P<0.05).ConclusionThe SF/P(LLA-CL) nanofibrous scaffold has good cell biocompatibility and can effectively promote tendon-bone healing, thus providing new method for modifying graft for ACL reconstruction in the clinical practice.
The study aimed to evaluate the safety and function of poly(lactic-acid-co-ε-caprolactone) (PLCL)/fibrinogen nanofibers (P/F-Ns), and provide theoretical basis for the clinical application. The surface morphology, mechanical properties, the hydrophilicity and the fibrinogen content of P/F-Ns were tested by scanning electron microscope, the material testing machine, the contact angle meter and the microplate reader, respectively. The cell adhesion, proliferation and ligament remodeling genes expression of Hig-82 cells on P/F-Ns were conducted through cell counting kit-8 (CCK-8) and real-time quantitative PCR analyses, respectively. The results showed that with the increase of the fibrinogen content, the pore sizes and hydrophilicity of three P/F-Ns increased, but the mechanical properties decreased. Cell adhesion and proliferation tests showed that P/F-N-2 held the best ability to promote cell adhesion and proliferation. The ligament remodeling genes expressions of Hig-82 cells on P/F-N-1, P/F-N-2 and P/F-N-3 were all up-regulated compared to P/F-N-0 on days 3 and 7. All the three P/F-Ns containing fibrinogen (P/F-N-1, P/F-N-2 and P/F-N-3) had better biocompatibility compared to P/F-N-0, and could be efficiently applied to the reconstruction of anterior cruciate ligament.