Objective To evaluate the osteogenesis of three bio-bone derived materials in repairing segmental bone defects. Methods Sixty Japanese rabbits were made 10 mm radius segmental defects and divided into 5 groups(groups A, B, C ,D and E,n=12). Composite fully deproteinised bone(CFDB, group A), partially deproteinised bone(PDPB, group B), partially decalcified bone(PDCB, group C), autogenous iliac bone graft(group D) and no implant(group E) were implanted into the radius segmental bone defects of rabbits. The specimens were examined after 4, 8, 12 and 24 weeks; the osteogenesis was evaluated through X-ray radiograph and undecalcified solid tissue histological examination.Results The border between the material and host’s bone was distinct after 4 weeks and blurred after 8 weeks; the density of partial edge of the material was similar to that of radii after 12 weeks. The medullary cavity of bone reopened in group B; the density of most defect area was similar to that of the host bone and there was a few high density shadow in group C; the density of most defect area was higher than that of host bone in group A after 24 weeks. There was no significant difference in radiograph scoring between groups A, B and C after 4 weeks and 8 weeks(P＞0.05); the scores of group B and C were higher than that of group A after 12 weeks(P＜0.05); and the scores were arranged as follow: group Dgt;group Bgt; group Cgt;group A after24 weeks(P＜0.05). Bone callusgrew toward defect area and new bone adhered to the material after 4 weeks and 8 weeks; more new bone formed, and the materials were absorbed and degraded with time. The quantity of bone formation was more in group D than in group B andin group B than in group C and in group C than in group A after 24 weeks(P＜0.05).Conclusion PDPB had good osteogenesis in repairing the segmental bone defect, PDCB was inferior to it, both PDPB and PDCB are fit to repair segmental bone defect. Both of them were inferior to autogenous bone.
Objective To investigate and compare the osteogenic potential of three kinds of calcium phosphate ceramic as carriers for recombinant human bone morphogenetic protein-2(rhBMP-2) in vivo.Methods BCPceramics (HA,TCP,HA/TCP) impregnated with rhBMP-2 (experimental groups) and without rhBMP-2(control groups) were implanted into 6 muscles pockets on the dorsum of 3month-old Wistar rabbits. The rabbits were sacrificed 2, 4 and 8 weeks after implantation and bone induction was estimated by alkaline phosphatase(ALP) activity measurement. The implants were also examined histologically and histomorphometrically by HE staining and computerized graphical analysis. Results The ALPactivity of implants withrhBMP-2 was higher than that of control groups(P＜0.05), but there was no difference between 2 and 4 weeks in experimental groups. In all experimental groups,theimplants exhibited that new bone formation increased with the lapse of time. The amount of new bone formation is more in -HA/rhBMP-2 group than in the other two group in the 2nd and 4th weeks, but there was no difference between them (P＞0.05).In the 8th week, the amount of bone formation was most in HA/TCP with -rhBMP-2, and was more than that in the 2nd and 4th weeks. Whereas in control groups, there was only fibrous connective tissue. Conclusion HA/TCP- is a good carriers of rhBMP-2 and can be used as bone substitutes clinically.