Mitochondrial adenosine triphosphate (ATP) synthase is the key enzyme of mitochondrial oxidative phosphorylation reaction.The down-regulation of the mitochondrial ATP synthase is a hallmark of most human carcinomas, which is the embodiment of the bioenergetic signature of cancer in the performance of the decreased oxidative phosphorylation and increased aerobic glycolysis. Combining with the bioenergetic signature of cancer, studies showed that mitochondrial ATP synthase and multidrug resistance and adverse prognosis of tumor were closely related. Its mechanisms are related to post-transcriptional regulation of the ATP synthase,the hypermethylation of the ATP synthase gene and the inhibitor peptide of the mitochondrial ATP synthase, called ATP synthase inhibitory factor 1(IF1). In this review, we stress the biological characteristics of mitochondrial ATP synthase and the relationship between ATP synthase and multidrug resistance and prognosis of Malignant tumor, in order to find a new way for tumor therapy.
ObjectiveTo fabricate the bionic scaffolds of rat spinal cord by combining three dimensional (3D) printer and 3D software, so as to lay the foundation of theory and technology for the manufacture of scaffolds by using biomaterials. MethodsThree female Sprague Dawley rats were scanned by 7.0T MRI to obtain the shape and position data of the cross section and gray matter of T8 to T10 spinal cord. Combined with data of position and shape of nerve conduction beam, the relevant data were obtained via Getdata software. Then the 3D graphics were made and converted to stereolithography (STL) format by using SolidWorks software. Photosensitive resin was used as the materials of spinal cord scaffolds. The bionic scaffolds were fabricated by 3D printer. ResultsMRI showed that the section shape of T8 to T10 segments of the spinal cord were approximately oval with a relatively long sagittal diameter of (2.20±0.52) mm and short transverse diameter of (2.05±0.24) mm, and the data of nerve conduction bundle were featured in the STL format. The spinal cord bionic scaffolds of the target segments made by 3D printer were similar to the spinal cord of rat in the morphology and size, and the position of pores simulated normal nerve conduction of rat spinal cord. ConclusionSpinal cord scaffolds produced by 3D printer which have similar shape and size of normal rat spinal cord are more bionic, and the procedure is simple. This technology combined with biomaterials is also promising in spinal cord repairing after spinal cord injury.
ObjectiveTo prepare bionic spinal cord scaffold of collagen-heparin sulfate by three-dimensional (3-D) printing, and provide a cell carrier for tissue engineering in the treatment of spinal cord injury. MethodsCollagen-heparin sulfate hydrogel was prepared firstly, and 3-D printer was used to make bionic spinal cord scaffold. The structure was observed to measure its porosity. The scaffold was immersed in simulated body fluid to observe the quality change. The neural stem cells (NSCs) were isolated from fetal rat brain cortex of 14 days pregnant Sprague-Dawley rats and cultured. The experiment was divided into 2 groups: in group A, the scaffold was co-cultured with rat NSCs for 7 days to observe cell adhesion and morphological changes;in group B, the NSCs were cultured in 24 wells culture plate precoating with poly lysine. MTT assay was used to detect the cell viability, and immunofluorescence staining was used to identify the differentiation of NSCs. ResultsBionic spinal cord scaffold was fabricated by 3-D printer successfully. Scanning electron microscope (SEM) observation revealed the micro porous structure with parallel and longitudinal arrangements and with the porosity of 90.25%±2.15%. in vitro, the value of pH was not changed obviously. After 8 weeks, the scaffold was completely degraded, and it met the requirements of tissue engineering scaffolds. MTT results showed that there was no significant difference in absorbence (A) value between 2 groups at 1, 3, and 7 days after culture (P>0.05). There were a lot of NSCs with reticular nerve fiber under light microscope in 2 groups;the cells adhered to the scaffold, and axons growth and neurosphere formation were observed in group A under SEM at 7 days after culture. The immunofluorescence staining observation showed that NSCs could differentiated into neurons and glial cells in 2 groups;the differentiation rate was 29.60%±2.68% in group A and was 10.90%±2.13% in group B, showing significant difference (t=17.30, P=0.01). ConclusionThe collagen-heparin sulfate scaffold by 3-D-printed has good biocompatibility and biological properties. It can promote the proliferation and differentiation of NSCs, and can used as a neural tissue engineered scaffold with great value of research and application.