To evaluate the effect of deacetylation degree (DDA) on the gelation behavior of thermosensitive chitosan-β glycerol phosphate disodium salt pentahydrate (CH-GP) system and to compare their rheological behaviors before and after gelation. Methods A series of thermosensitive CH-GP samples with different DDAs (70%, 85%, 90%, 97%)were prepared by dissolving CH with 0.1 mol/L HCl solution, 5 samples for every single DDA, and then all these CH-GP solution samples processed the frequency sweep test and temperature sweep test (10-70℃ , 1℃ /min) on AR 2000ex rheometer, with pH value of 7.02. Also, all the results of hydrogel samples were processed a frequency sweep test. Results With CH concentration of 2% (w/v) and pH value of 7.02 , the gelating temperature of CH-GP systems with different DDAs (85%, 90%, 97%) were (59.90 ± 0.08), (48.10 ± 0.08), (37.10 ± 0.11) ℃ , respectively. While the gelating temperature of CH-GP system with 70% DDA was over 70℃ . There were statistically significant differences in temperature and time of gelation among groups with different DDAs (P lt; 0.05). Furthermore, storage modulus of such system raised from dozens Pa to a magnitude of several kPa during gelation , while loss modulus kept almost steady. Conclusion Gelating temperature and mechanical property of the system could be measured objectively by rheological characterization. Thus during designing tissue engineered scaffolds for various purposes, it is helpful applying selected CH with optimal DDA to different target tissues.
Objective To investigate the latest development of tissue engineeredregenerative medicine in industrialization, with the intention to direct work in practical area. Methods A complete insight of regenerative medicine in industrialization was obtained through referring to update publications, visiting related websites, as well as learning from practical experience. Results The aerial view of the future of regenerative medicine was got based on knowledge of four different tissue engineering projects. Conclusion All present efforts should be devoted to regenerative medicine area meeting the industrialized trends.