ObjectiveThe antibacterial properties of porous medical implant materials were reviewed to provide guidance for further improvement of new medical implant materials.MethodsThe literature related to the antibacterial properties of porous medical implant materials in recent years was consulted, and the classification, characteristics and applications, and antibacterial methods of porous medical implant materials were reviewed.ResultsPorous medical implant materials can be classified according to surface pore size, preparation process, degree of degradation in vivo, and material source. It is widely used in the medical field due to its good biocompatibility and biomechanical properties. Nevertheless, the antibacterial properties of porous medical implant materials themselves are not obvious, and their antibacterial properties need to be improved through structural modification, overall modification, and coating modification.ConclusionAt present, coating modification as the mainstream modification method for improving the antibacterial properties of porous medical materials is still a research hotspot. The introduction of new antibacterial substances provides a new perspective for the development of new coated porous medical implant materials, so that the porous medical implant materials have a more reliable antibacterial effect while taking into account biocompatibility.
Objective To design and construct a graphene oxide (GO)/silver nitrate (Ag3PO4)/chitosan (CS) composite coating for rapidly killing bacteria and preventing postoperative infection in implant surgery. Methods GO/Ag3PO4 composites were prepared by ion exchange method, and CS and GO/Ag3PO4 composites were deposited on medical titanium (Ti) sheets successively. The morphology, physical image, photothermal and photocatalytic ability, antibacterial ability, and adhesion to the matrix of the materials were characterized. Results The GO/Ag3PO4 composites were successfully prepared by ion exchange method and the heterogeneous structure of GO/Ag3PO4 was proved by morphology phase test. The heterogeneous structure formed by Ag3PO4 and GO reduced the band gap from 1.79 eV to 1.39 eV which could be excited by 808 nm near-infrared light. The photothermal and photocatalytic experiments proved that the GO/Ag3PO4/CS coating had excellent photothermal and photodynamic properties. In vitro antibacterial experiments showed that the antibacterial rate of the GO/Ag3PO4/CS composite coating against Staphylococcus aureus reached 99.81% after 20 minutes irradiation with 808 nm near-infrared light. At the same time, the composite coating had excellent light stability, which could provide stable and sustained antibacterial effect. ConclusionGO/Ag3PO4/CS coating can be excited by 808 nm near infrared light to produce reactive oxygen species, which has excellent antibacterial activity under light.