Objective To develop a tissue engineering scaffold by using 4arm branched polyethylene glycol-VS (PEG-VS) crosslinked with decellularized valved conduits (DVC), and to research on its mechanical and biological functions. Methods The valved aortic conduits of rabbits were taken and decellularized by trypsin method and then were crosslinked with 4arm branched PEG-VS to construct the composite scaffolds (CS). The functions of decellularized valved conduits and the composite scaffolds were tested by mechanics test system. Thirty New Zealand white rabbits were equally and randomly assigned to one of the three groups: the control group, the DVC group, and the CS group. Valved aortic conduits, decellularized valved conduits and composite scaffoldswere transplanted into the common carotid artery of the abovementioned three groups of rabbits respectively. Twentyeight days after the operation, patency of the transplants was tested by Color Doppler ultrasound; micromorphology and inflammatory infiltration were observed by hematoxylin eosin（HE） staining andscanning electron microscope (SEM)，and endothelialization of composite scaffolds was detected by immunofluorescent staining. Results A series of biomechanical analyses revealed that the composite scaffolds had highly similar mechanical properties as fresh tissue, and had superior elastic modulus (P=3.1×10-9) and tensile strength (P=1.1×10-6) compared with decellularized valved conduits. Color Doppler ultrasound revealed that the graft patency for the CS group was better than the control group (P=0.054) and the DVC group (P=0.019), and the intraaortic thrombosis rate and distortion rate decreased significantly. HE staining and SEM showed that the endothelialization of composite scaffolds in the CS group was significantly higher than the other two groups with the endothelial cells evenly distributed on the scaffolds. The [CM(159mm]immunofluorescent staining indicated that the positive rate of the endothelial cell marker CD34 was higher than the other two groups. Conclusion The composite scaffolds using 4arm branched PEGVS crosslinked with DVC have great mechanical and biological properties.

Citation： LIU Junwei,DONG Nianguo,SHI Jiawei,et al .. An Experimental Study of Decellularized Valved Conduits Crosslinked with 4arm Branched Polyethylene GlycolVS. Chinese Journal of Clinical Thoracic and Cardiovascular Surgery, 2011, 18(4): 332-337. doi: Copy