The objective of this research is to evaluate the effects of different silane coupling agents on the bond strength between Ceramco3 opaque porcelain and indirect composite resin. Five groups of Co-Cr metal alloy substrates were fabricated according to manufacturer's instruction. The surface of metal alloy with a layer of dental opaque porcelain was heated by fire. After the surface of opaque porcelain was etched, five different surface treatments, i.e. RelyX Ceramic Primer (RCP), Porcelain Bond Activator and SE Bond Primer (mixed with a proportion of 1:1) (PBA), Shofu Porcelain Primer (SPP), SE bond primer (SEP), and no primer treatment (as a control group), were used to combine P60 and opaque porcelain along with resin cement. Shear bond strength of specimens was tested in a universal testing machine. The failure modes of specimens in all groups were observed and classified into four types. Selected specimens were subjected to scanning electron microscope and energy disperse spectroscopy to reveal the relief of the fracture surface and to confirm the failure mode of different types. The experimental results showed that the values of the tested items in all the tested groups were higher than that in the control group. Group PBA exhibited the highest value[(37.52±2.14) MPa] and this suggested a fact that all of the specimens in group PBA revealed combined failures (failure occurred in metal-porcelain combined surface and within opaque porcelain). Group SPP and RCP showed higher values than SEP (P<0.05) and most specimens of SPP and RCP performed combined failures (failure occurred in bond surface and within opaque porcelain or composite resin) while all the specimens in group SEP and control group revealed adhesive failures. Conclusions could be drawn that silane coupling agents could reinforce the bond strength of dental composite resin to metal-opaque porcelain substrate. The bond strength between dental composite resin and dental opaque porcelain could meet the clinical requirements.
This paper is aimed to investigate the effect of rest-inserted loading on the mechanosensitivity of osteocytes. In the investigation, cultured MLO-Y4 osteocyte-like cells were strained on cyclic compressive force (CCF) by the self-made compressive loading device. Then we observed the effect of different rest periods-inserted loading (5 s, 15 s, 30 s, respectively) on the mechanosensitivity of osteocytes. We then determined the levels of secreted nitric oxide (NO) and prostaglandin E2 (PGE2) by Griess method and enzyme linked immunosorbent assay (ELISA), respectively. We then stained the cytoskeleton F-actin using immunofluorescence. We found that the expressions of NO and PGE2 in rest-inserted strained groups (>15 s) were significantly increased compared to those in the continuous strained group. And rest-inserted loading promoted the parallel alignment of stress fibers. It indicates that rest-inserted loading could promote the mechanosensitivity of osteocytes, and this might be related to the parallel alignment of stress fibers.